How to use Best EPOXY DECORATION ADHESIVE


Best EPOXY DECORATION ADHESIVE is based on epoxy resin to reprocess or modify its properties to make its performance parameters meet specific requirements. Epoxy resin glue is generally only used in conjunction with a curing agent, and can be completely cured after mixing evenly. Best EPOXY DECORATION ADHESIVE is generally called glue A or main agent, and curing agent is called glue B or curing agent.

Best EPOXY DECORATION ADHESIVE

How to use Best EPOXY DECORATION ADHESIVE
1. Remove dust, oil, rust, etc. with dry cotton cloth or sandpaper. On the next surface, then use acetone or trichloroethylene and other cleaners to clean the next surface.
2. Unscrew the front cover, fully mix the A + B agent according to the above weight ratio, and then use it; in order to ensure the use effect, vacuum can also be used.
3. It should be noted that it must be used up within the operational time, otherwise it will cure, resulting in material waste, and the highest strength can be obtained after 24 hours.
4. After gluing, cure at room temperature at 40-50℃ for 2-6 hours, curing time is 1-3 hours; use after gluing for 24 hours; better adhesion after 10 days. In cold and humid weather, a room temperature of 15 ~ 25 ℃ is required for bonding.
5. When gluing straight and inverted surfaces, the adhesive must be taped or positioned with 502 glue. Best EPOXY DECORATION ADHESIVE formula epoxy resin AB adhesive is a two-component high temperature resistant adhesive based on epoxy resin, mainly used for bonding high temperature resistant metals, ceramics, etc. The operating temperature is - 50 - + 180 °C and can reach + 250 °C for short periods of time.
 

*Note:We will get in touch with you as soon as possible

message

Related News


Questions and answers about MODIFIED ACRYLIC AB ADHESIVE (BOXES)

MODIFIED ACRYLIC AB ADHESIVE (BOXES) uses methyl methacrylate as the main raw material, with tougheners, reinforcing agents, stabilizers, initiators, polymerization inhibitors, etc., two components synthesized through advanced technology (A, B) Reactive structural adhesive.