Bonding metal, glass, ceramic, marble, wood and many rigid plastics.
Not Recommended For :
Polyethylene, polypropylene, Nylon,Teflon or flexible materials.
Applying at temperatures lower than -60°C or above 100°C.
Continuously wet areas or water immersion.
Application Method
(1). Surface of adherent has to be cleaned, dried.
(2). A/B components should be mixed 1:1 in weight in proper amount. Usually, initial curing can be reached within
5-10Minutes(25°C) and available in 1 hours. full Bonded joint can be used after 24 hours.
(3). After bonding the product, according to the requirements of the bonding process on the treatment, so as not to affect the
effect.
(4). This product is partial thick, will be a normal phenomenon and does not affect the bonding effect.
Application
(1). Surface of adherent has to be cleaned, dried.
(2). A/B components should be mixed 1:1 in weight in proper amount. Usually, initial curing can be reached within
5-10Minutes(25°C) and available in 1 hours. full Bonded joint can be used after 24 hours.
(3). After bonding the product, according to the requirements of the bonding process on the treatment, so as not to affect the
effect.
(4). This product is partial thick, will be a normal phenomenon and does not affect the bonding effect.
Application
Technical Parameters
Color A: green; B: red;
Viscosity (cps/25℃) A:4000~6000; B:4000~6000
Operation time (25℃/100g) 5 minutes
Curing time (25℃/100g) surface dry: 5~10 minutes, full cure: 24 hours
Shear strength (MPa) ≥16
Impact resistance (kj/m2) ≥18
Temperature (℃) -60~+100
Shelf life 12 months
Color A: green; B: red;
Viscosity (cps/25℃) A:4000~6000; B:4000~6000
Operation time (25℃/100g) 5 minutes
Curing time (25℃/100g) surface dry: 5~10 minutes, full cure: 24 hours
Shear strength (MPa) ≥16
Impact resistance (kj/m2) ≥18
Temperature (℃) -60~+100
Shelf life 12 months